| 1. | The effects of doping ratio , calcinations temperature and calcinations time on the structure and the particle size have been comprehensively studied
系统研究了掺杂比，热处理温度，热处理时间等制备工艺过程对ato纳米粉体相组成和粉体粒度的影响。 | | 2. | The appropriate calcinations temperature is about 700 , and the tetragonal sno2 phase crystal structure of the particles remained unchanged when sb was doped to it . as the calcinations temperature increasing and the calcinations time prolong , the size of particles grows and the crystallization tend to be complete . study on the electrical properties of ato powders prepared by hydrothermal synthesis was performed in - depth , the most optimal electrical properties are obtained at doping ratio of 11 percent
水热法制备的ato纳米粉体在热处理温度700左右较为适宜，锑的掺杂并未改变粉体的四方相金红石结构，随锑掺杂量的增加，粉体的粒度变小；随热处理温度的升高和热处理时间的延长， ato粉体的粒度增大，晶体结构趋于完整。 | | 3. | Using sncl4 - 5h2o and sbcl3 as precursors , antimony doped tin oxide particles with good electrical properties have been prepared by hydrothermal synthesis . the optimal conditions of this synthesis process were as following : doping ratio was 11 % ; reaction temperature was 180 ; reaction time was 2h ; the temperature and time of calcinations is 700 and 2h . the size of ato particles obtained is about 20nm , and its resistance can reach 0 . 2 , under 0 . 2mpa pressure
在掺杂浓度为11 ，水热反应温度为180 ，反应压力1mpa ，反应时间2h ，热处理温度为700 ，热处理时间2h的实验条件下制备的ato粉体，性能达到最佳，晶粒度在20个nm左右，在0 . 2mpa压力下粉体电阻值为0 . 2 。 |
- Similar Words：
- "doping of gasoline" English translation, "doping of semiconductor" English translation, "doping print" English translation, "doping profile" English translation, "doping profiler" English translation, "doping shot" English translation, "doping system" English translation, "doping technology" English translation, "doping temperature" English translation, "doping test" English translation
|
|
|